Bearing layer of OMT-106 is composed of excellent designed woven structure of PTFE fiber and high strength synthetic fibers with specially formulated solid lubricant additions.
OMT-106 composite bearings maintain high compressive strength with fiberglass-epoxy backing layer which is manufactured at a specific angle by filament winding process.
OMT-106 is self-lubricating sliding composite bearing with high load carrying capacity to be applied under slow speed rotating, oscillating and reciprocating movements.
OMT-106bearings have excellent wear resistance property and very good resistance against shock, vibration loads.
There are two types of bushes in OMT-106, SF-A and SF-B which difference as per application.
|Maximum specific load Static||N/mm2 Psi||250 36250|
|Maximum specific load dynamic||N/mm2 Psi||140 20000|
|Maximum sliding speed||m/s fpm||0.25 50|
|Maximum PxV factor||N/mm2;x m/s||1.6|
|Maximum PxV factor||N/mm2;x m/s||1.9|
|Dry coefficient of friction||µm||0.03 - 0.12|
|Shaft finish Ra (recommended)||µm||0.4 Ra|
|Shaft hardness (recommended)||HB||>350|